[en] Crack velocity curves for Y-TZP and Al₂O₃-toughened Y-TZP were determined for long cracks in compact tension specimens with an in situ fracture device on the stage of an optical microscope. Indications for a crack velocity threshold were found for both materials. It is recognized that the dependence of the shielding term on the crack-tip stress field renders transformation-toughened materials particularly susceptible to stress-corrosion cracking. This interrelation leads to the definition of a steady-state velocity at constant applied stress intensity factor. This velocity is obtained in the situation where the shielding term is fully defined by the present crack-tip stress field, not depending on prior loading history