[en] For examining the crack growth under conditions of superimposed creep and fatigue stress, fatigue crack growth tests with hold times (30 sec. up to 4 hours), tests with non-linear loading for various time periods, and tests combining sequential periods of pure creep or pure fatigue stress have been performed with 25 mm CT specimens of the iron base alloy 800 (X10NiCrAlTi 32 20) at an elevated temperature of 700 C. At this temperature, the material exhibits at about equal stress levels approximately equal contributions of creep crack growth and fatigue crack growth. The crack growth behaviour during hold periods and under non-linear stress is described using the characteristics of pure creep crack growth or fatigue crack growth, in the frame of a linear damage accumulation model. (orig.)
[de]
Zur Untersuchung des Risswachstums unter ueberlagerter Kriech- und Ermuedungsbeanspruchung wurden Ermuedungsrisswachstumsversuche mit Haltezeiten (30 Sekunden bis 4 Stunden), Versuche mit rampenfoermiger Belastung unterschiedlicher Periodendauer sowie Versuche mit hintereinandergeschalteten Perioden reinen Kriech- und Ermuedungsrisswachstums an 25 mm-CT-Proben der Eisenbasislegierung Alloy 800 (X10NiCrAlTi 32 20) bei 700 C durchgefuehrt. In diesem Temperaturbereich weist dieser Werkstoff bei gleichem Spannungsniveau etwa gleichwertige Anteile von Kriech- und Ermuedungsrisswachstum auf. Das Risswachstum in Haltezeit- und Rampenversuchen wird mit den Kenngroessen des reinen Kriechrisswachstums und Ermuedungsrisswachstums auf der Basis eines linearen Schadensakkumulationsansatzes beschrieben. (orig.)Source
Schriftenreihe Reaktorsicherheit und Strahlenschutz; 1993; 132 p; ISSN 0724-3316; 
; ISSN 0724-3316; ; FOERDERKENNZEICHEN BMU SR 0417; Available from FIZ Karlsruhe
; ISSN 0724-3316; ; FOERDERKENNZEICHEN BMU SR 0417; Available from FIZ Karlsruhe