[en] Post-exposure annealing of highly sensitive LiF:Mg,Cu,P (MCP-N) detectors, at 100 deg. C over 10 or 20 min prior to readout, is usually recommended for routine dosimetry. The purpose of this anneal is to eliminate low-temperature peaks, especially peak 3, which fades at room temperature in about 3 months. However, as this annealing procedure does not entirely eliminate peak 3, 10% of its thermoluminescent (TL) signal still being readable, a fading correction must be applied. The aim of this work was to optimise the conditions of post-exposure treatment, i.e. its temperature and duration, in order to facilitate the use of MCP-N detectors in routine dosimetry. MCP-N detectors were annealed in standard conditions, i.e. at 240 deg. C over 10 min and exposed to a dose of 5 mGy (¹³⁷Cs). For post-exposure annealing, six different temperatures between 100 deg. C and 150 deg. C and two time periods (10 and 20 min) were tested. TL glow curves were deconvoluted with the GCA code. A post-exposure anneal at 120 deg. C over 10 min was found to be optimal. Heating at this temperature eliminates 100% of the TL signal of peak 3, while maintaining the area and maximum intensity of the main peak 4 unchanged. In this case, no fading correction needs to be applied. Annealing at higher temperatures, up to 150 deg. C, results in a loss of peak 4 signal, and is therefore not recommended. (author)