[en] The VHTR (Very High Temperature Gas Reactor) is one of the reactor concepts in the Gen IV International Collaboration. The nuclear fuel of a VHTR in the US is based on microspheres containing a mixture of UO₂ and UC₂ coated with multi carbon layers and a SiC layer. This mixture is called a 'UCO (uranium oxi carbide)' kernel. The fabrication process of this kernel was based on the sol-gel method between an ADUN and HMTA and urea, a process referred to as internal gelation. UCO kernel microspheres were first prepared at ORNL in the late 1970s. CB(Carbon Black) as a carbon source in the final UCO kernel is added during the broth solution preparation, in the processing of UCO kernel fabrication. The preparation of a good quality UCO kernel is very difficult due to the homogeneous distribution of carbon in a UCO kernel. The key requirement to obtain a good quality kernel is a uniform distribution of carbon in the ADU gel sphere forming process before the thermal treatment, i.e., during the gel formation step. The internal gelation concept was adapted in ADU gel sphere fabrication in the ORNL process of the US. Generally, UO₂ kernel microspheres are prepared by an internal gelation method (USA, India) or external gelation method (Germany, China, Japan). The UCO kernel microspheres prepared only in the US, use an internal gelation method. A material flow chart on the preparation of the microsphere kernel is simply shown in Fig. 1. The broth solution preparation, the raw material, additives, and thermal steps such as calcining and sintering processes were different to compared with the external gelation and internal gelation methods. In this study, we first carried out the matching CB selection experiments among the various kinds of CBs in a broth solution, for UCO kernel preparation using an external gelation method.