L.T. Corredor, D.A. Landínez Téllez, J.L. Pimentel Jr, P. Pureur, J. Roa-Rojas
DOI: 10.4236/jmp.2011.23023   PDF    HTML     5,158 Downloads   10,521 Views   Citations

Abstract

We report structural, morphological and magnetic properties of the Sr₂GdRuO₆ compound, which is used as precursor oxide in the production process of RuSr₂GdCu₂O₈ superconducting ruthenocuprates. The crystalline structure was studied by X-ray diffraction and Rietveld refinement. Results reveal that material crystallizes in a monoclinic double perovskite, space group P21/n (#14). Scanning Electron Microscopy experiments on samples show homogeneous granular morphology with grain size from 3 up to 7 μm. Semiquantitative analysis of composition was performed by the Energy Dispersive X-ray technique. Experimental results are 98% in agreement with the theoretical stoichiometry. Curves of magnetization as a function of temperature exhibit an antiferromagnetic-like behaviour, with Néel temperature TN=15.3 K and magnetic effective moment 8.72μB.

Keywords

Complex Perovskite, Structure, Magnetic Properties

Share and Cite:

Conflicts of Interest

The authors declare no conflicts of interest.

References

[1]	L. Bauerfeind, W. Widder and H. F. Braun, Physica C, Vol. 254, 1995, p. 151. doi:10.1016/0921-4534(95)00574-9
[2]	T. P. Papageorgiou, T. Herrmannsd?rfer, R. Dinnerbier, T. Mai, T. Ernst, M. Wunschel and H. F. Braun, Physica C , Vol. 377, 2002, p. 383. doi:10.1016/S0921-4534(01)01291-6
[3]	L. T. Yang, J. K. Liang, Q. L. Liu, C. Q. Jin, X. M. Feng, G. B. Song, J. Luo, F S. Liu and G. H. Rao, Journal of Solid State Chemistry, Vol. 177, 2004, p. 1072. doi:10.1016/j.jssc.2003.10.015
[4]	L. T. Corredor, J. Velasco Zárate, D. A. Landínez Téllez, F. Fajardo, J. Arbey Rodríguez and M. J. Roa-Rojas, Physica B, Vol. 404, 2009, p. 2733. doi:10.1016/j.physb.2009.06.078
[5]	T. Nachtrab, C. Bernhard, C. T. Lin, D. Koelle and R. Kleiner, C. R. Physique, Vol. 7, 2006, p. 6885. doi:10.1016/j.crhy.2005.11.010
[6]	A. A. Vasiliev, M. Aindow, Z. H. Han, J. I. Budnik, W. A. Hines, P. W. Klamut, M. Maxwell and B. Dabrowski, Applied Physic Letters, Vol. 85, 2004, p. 3217. doi:10.1063/1.1805176
[7]	C. Bernhard, J. L. Tallon, C. Niedermayer, T. Blasius, A. Golnik, E. Br¨ucher, R. K. Kremer, D. R. Noakes, C. E. Stronach, and E. J. Ansaldo, Physical Review B, Vol. 59, 1999, p. 14099. doi:10.1103/PhysRevB.59.14099
[8]	J. D. Jorgensen, O. Chmaissem, H. Shaked, S. Short, P. W. Klamut, B. Dabrowski, J. L. Tallon, Physical Review B, Vol. 63, 2003, p. 054440. doi:10.1103/PhysRevB.63.054440
[9]	A. C. Larson and R. B Von Dreele, “General Structure Analysis System (GSAS),” Los Alamos National Laboratory Report LAUR, 2000, p. 86.
[10]	M. W. Lufaso and P. M. Woodward, Acta Crystallographica B, Vol. 57, 2001, p. 725. doi:10.1107/S0108768101015282
[11]	C. J. Howard, B. J. Kennedy and P. M. Woodward, Acta Crystallographica B, Vol. 59, 2003, p. 463. doi:10.1107/S0108768103010073
[12]	R. Sáez-Puche, E. Climent-Pascual, R. Ruiz-Bustos, M. A. Alario-Franco and M. T. Fernández-Díaz, Progress in Solid State Chemistry Vol. 35, 2007, p. 211. doi:10.1016/j.progsolidstchem.2007.02.001
[13]	Y. Doi and Y. Hinatsu, Journal of Physics Condensed Matter, Vol. 11, 1999, p. 4813. doi:10.1088/0953-8984/11/25/302
[14]	N. W. Ashcroft and N. D. Mermin, Solid State Physics, Saunders College Publishing, Fort Worth, 1976, p. 657.